    首頁 > 技術文章 > 1.1191物理性質
    
      
    
      
    
        
    1.1191物理性質
    
        
    點擊次數：838更新時間：2022-03-07
    
        
    Chemical composition % of steel C45E (1.1191): EN 10277-5-2008
    Cr + Mo + Ni = 0.63
    CSiMnNiPSCrMo
    0.42 - 0.5max 0.40.5 - 0.8max 0.4max 0.03max 0.035max 0.4max 0.1

    New opportunities for buyers!
    Post free buying requirement of steel C45E (1.1191)


    Mechanical properties of steel C45E (1.1191)

    Nominal thickness (mm):to 1616 - 100100 - 250250 - 500500 - 1000






    Rm - Tensile strength (MPa) (+N)620580560540530
    Nominal thickness (mm):0.3 - 3


    Rm - Tensile strength (MPa) (+A)570
    Nominal thickness (mm):0.3 - 3


    Rm - Tensile strength (MPa) (+CR)1020
    Nominal thickness (mm):5 - 1010 - 1616 - 4040 - 6363 - 100






    Rm - Tensile strength (MPa) (+C)750-1050710-1030650-1000630-900580-850
    Nominal thickness (mm):to 88 - 2020 - 5050 - 80





    Rm - Tensile strength (MPa) (+QT)700650630600


    Nominal thickness (mm):to 88 - 2020 - 5050 - 80





    ReH - Minimum yield strength (MPa) (+QT)490430370340


    Nominal thickness(mm):to 1616 - 100100 - 250250 - 500500 - 1000






    Re - Upper yield strength or
    Rp0.2 - 0.2% proof strength (MPa) (+N)    		340305275240230
    Nominal thickness(mm):0.3 - 3


    Rp0.2 0.2% proof strength (MPa) (+A)455
    Nominal thickness(mm):5 - 1010 - 1616 - 4040 - 6363 - 100






    Rp0.2 0.2% proof strength (MPa) (+C)565500410360310




    KV - Impact energy (J) transverse, (+QT)+20°
    14


    KV - Impact energy (J) longitud., (+QT)+20°
    25-50


    Nominal thickness (mm):0.3 - 3


    A - Min. elongation Lo = 80 mm (%) (+A)18
    Nominal thickness (mm):5 - 1010 - 1616 - 4040 - 6363 - 100






    A - Min. elongation at fracture (%) (+C)56788
    Nominal thickness (mm):to 88 - 2020 - 5050 - 80





    A - Min. elongation at fracture (%) longitud., (+QT)14161717


    Nominal thickness (mm):to 1616 - 100100 - 250




    A - Min. elongation Lo = 5,65 √ So (%) (+N)141616


    <tdZ - Reduction in cross section on fracture (%) (+QT)

    40


    Brinell hardness (HBW): (+S)255
    Brinell hardness (HBW): (+A)207
    Brinell hardness (HBW): (+SH)172 - 242
    Vickers hardness ( HV): (+CR)290
    Vickers hardness ( HV): (+A)180


    Properties of steel C45E (1.1191)
    Weldability: Due to the medium-high carbon content it can be welded with some precautions.
    Hardenability: It has a low hardenability in water or oil; fit for surface hardening that gives this steel grade a high hardness of the hardened shell.


    Equivalent grades of steel C45E (1.1191)
    Warning! Only for reference
    EU
    EN    		USA
    -    		Germany
    DIN,WNr    		Japan
    JIS    		France
    AFNOR    		England
    BS    		Italy
    UNI    		Spain
    UNE    		China
    GB    		Sweden
    SS    		Finland
    SFS    		Russia
    GOST    		Inter
    ISO
    C45E
    1045
    Ck45
    S45C
    XC45
    XC48H1
    080M46
    CFS8
    C45
    C45k
    F1140
    45
    45H
    1672
    C45
    45
    C45E4

    
        
      
    
    
    
  
    

    

    
  
    
    
    
      